3.62V 2850mAh LG 18650 MG1 battery – LGMG11865
LG18650MG1–(LGMG11865 3.62V )
The LG 18650 MG1 battery – LGMG11865 battery comes up with a nominal capacity of 2850mAh, the voltage of 3.62V .
The LG MG1 is a lithium-ion cell intended for use in 18650 battery packs. It can power a wide range of devices including a table lamp, exercise equipment, or drain cleaner.
This is an absolutely excellent cell for anyone seeking high performance 18650 cells.
HIGHLIGHTS OF LG18650 MG1
Chemistry: NCM
Max. continuous discharge current: 30A
Nominal capacity: 2850mAh
Minimum capacity: 2750mAh
Nominal voltage: 3.62V
Standard charge current: 1425mA
Maximum charge current: 2850mA
Charge voltage: 4.2V
Charge cut-off current: 50mA
Standard discharge 570mA
End voltage: 2.5V
Maximum discharge current: 10A
Cycle life: 500 cycles to 70% at standard charge/discharge.
Operating temperature: Charge: 0°C ~ 45°C, Discharge: -20°C ~ 60°C
Storage temperature: 1 month: -20°C ~ 60°C, 3 months: -20°C ~ 45°C, 1 year: -20°C ~ 20°C
Max. Discharge Current: 1075mA / 4300mA
APPLICATION: light electric vehicle, a table lamp, exercise equipment, or drain cleaner—wide usage
APPEARANCE
There shall be no such defects as deep scratch, crack, rust, discoloration or leakage, which may adversely affect the commercial value of the cell.
Diameter : 18.3 + 0.1/-0.3 mm ( Max. 18.4 mm )Diameter is defined as the largest data value measured on the “A” area of a cylindrical cell.
Height : 65.0 ± 0.2 mm ( Max. 65.2 mm )
Nominal Specification of LG-18650-MG1
Item | Condition | Specification |
---|---|---|
Capacity | Std. charge / discharge | Nominal 2,850 mAh (Cnom) |
Minimum 2,750 mAh (Cmin) | ||
Nominal Voltage | Average for Std. discharge | 3.62V |
Standard Charge | Constant current | 0.5C (1,425mA) |
Constant voltage | 4.2V | |
End condition(Cut off) | 50mA | |
Max. Charge Voltage | - | 4.2V |
Max. Charge Current | - | 1.0C(2,850mA) |
Standard Discharge | Constant current | 0.2C (570mA) |
End voltage(Cut off) | 2.5V | |
Max. Discharge Current | - | 10A |
Weight | Approx. | 46.0 g |
Operating Temperature | Charge | 0 ~ 45℃ |
Discharge | -20 ~ 60℃ | |
Storage Temperature (for shipping statei) | 1 month | -20 ~ 60℃ |
3 month | -20 ~ 45℃ | |
1 year | -20 ~ 20℃ |
Performance Specification
4.1.1 Standard Charge
Unless otherwise specified, “Standard Charge” shall consist of charging at constant current of 1,425mA. The cell shall then be charged at constant voltage of 4.2V while tapering the charge current. Chargingshall be terminated when the charging current has tapered to 50mA. For test purposes, charging shall be performed at 25ºC ± 2ºC
4.1.2 Standard Discharge
“Standard Discharge” shall consist of discharging at a constant current of 570mA to 2.5V. Discharging is to be performed at 25 ºC ± 2 ºC unless otherwise noted (such as capacity versus temperature).
4.1.3 Fast Charge / discharge condition
Cells shall be charged at constant current of 1,000mA to 4.2V with end current of 100mA. Cells shall be discharged at constant current of 6,000mA to 2.75V. Cells are to rest 5 minutes after charge and 5 minutes after discharge.
Item | Condition | Specification |
---|---|---|
Initial AC Impedance | Cell shall be measured at 1kHz after charge per standard charge | ≤35mΩ,without PTC |
InitialCapacity | Cellsshallbechargedper standard charge and discharged per standard discharge within 1h after full charge | Cini≥2,750mAh (Cmin) |
CycleLife | Cells shall be charged and discharged per high drain rate charge,500cycles.A cycle is defined as one charge and one discharge.501st discharge capacity shall be measured per standard charge and standard discharge | ≥70%(of Cminin2.1) |
Item | Condition | Specification | |
---|---|---|---|
Storage Characteristics | Cells shall be charged per standard charge and stored in a temperature-controlled environment at 25ºC ± 2ºC for 30 days. After storage, cells shall be discharged per standard discharge to obtain the remaining capacity.* | Capacity remaining rate ≥ 90% (Cini in 2.1) | |
High Temperature Storage Test | Cells shall be charged per standard charge and stored in a temperature-controlled environment at 60ºC for 1 week. After storage, cells shall be discharged per standard discharge and cycled per standard charge and standard discharge for 3 cycles to obtain recovered capacity*. | No leakage, Capacity recovery rate ≥ 80% of Cini | |
Thermal Shock Test | 65ºC (8h) ← 3hrs → -20ºC (8h) for 8 cycles with cells charged per standarf charge After test, cells are discharged per Standard Discharge and cycled per Standard Charge and Standard Discharge for 3 cycles to obtain recovered capacity. | No leakage Capacity recovery rate ≥ 80% of Cini | |
High Temperature and High Humidity Test | Cells are charged per standard charge and stored at 60ºC (95% RH) for 168 hours. After test, cells are discharged per standard discharge and cycled per standard charge and standard discharge for 3 cycles to obtain recovered capacity. | No leakage, No rust Capacity recovery rate ≥ 80% | |
Temperature Dependency of Capacity | Cells shall be charged per standard charge at 25ºC ± 2ºC and discharged per standard discharge at the following temperatures. | ||
Charge | Discharge | Capacity | |
25℃ | -10℃ | 60% of Cini | |
0℃ | 80% of Cini | ||
23℃ | 100% of Cini | ||
60℃ | 95% of Cini |
* Remaining Capacity : After storage, cells shall be discharged with standard condition(4.1.2) to measure the remaining capacity.
** Recovery Capacity : After storage, cells shall be discharged with standard discharge condition(4.1.2), and then cells shall be charged with standard charge condition(4.1.1), and then discharged with standard discharge condition(4.1.2). This charge / discharge cycle shall be repeated three times to measure the recovery capacity
Warning:
1). Do not disassemble, dispose of in fire, heat or short circuit.
2).Do not insert batteries with the(+)and(-)reversed.
3). Do not mix fresh batteries with used batteries.
4).Do not submerge the battery in water
Want More Details: Download our battery design ebook.Lithium Battery Design Design Ebook Download(2M, 20 pages, PDF)
How to Custom 18650 Battery Pack
We have the unique ability to develop custom 18650 battery pack to fit your needs. Our expert team of chemists, engineers, and manufacturers who use proven chemistry and production methods that will get from spec to production fast. Slim, flexible, more powerful.